Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application.
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application./
作者:
Eiliat, Hoda.
面頁冊數:
214 p.
附註:
Source: Dissertation Abstracts International, Volume: 76-10(E), Section: B.
Contained By:
Dissertation Abstracts International76-10B(E).
標題:
Automotive engineering. -
電子資源:
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3706512
ISBN:
9781321804256
Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application.
Eiliat, Hoda.
Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application.
- 214 p.
Source: Dissertation Abstracts International, Volume: 76-10(E), Section: B.
Thesis (Ph.D.)--University of Windsor (Canada), 2015.
This item must not be sold to any third party vendors.
Automotive industry strives to reach an optimum level of fuel economy. This can be achieved by overcoming two impacting factors on fuel consumption: weight and friction force. This research contributes to reduce both. The proposed surface treatment can replace cylinder liners of hypoeutectic aluminum silicon alloy engine blocks with a thin layer of ceramic oxide composed of alpha and gamma phases of Al2O3 and mullite. The coatings are achieved in an aqueous electrolytic bath with current densities of 0.1 to 0.2 A/cm2.
ISBN: 9781321804256Subjects--Topical Terms:
2181195
Automotive engineering.
Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application.
LDR
:02469nmm a2200325 4500
001
2063914
005
20151102092431.5
008
170521s2015 ||||||||||||||||| ||eng d
020
$a
9781321804256
035
$a
(MiAaPQ)AAI3706512
035
$a
AAI3706512
040
$a
MiAaPQ
$c
MiAaPQ
100
1
$a
Eiliat, Hoda.
$3
3178468
245
1 0
$a
Tribological Study on Plasma Electrolytic Oxidation Treatment in Al-Si Alloys for Engine Application.
300
$a
214 p.
500
$a
Source: Dissertation Abstracts International, Volume: 76-10(E), Section: B.
500
$a
Advisers: Xueyuan Nie; Jimmi S.Y. Tjong.
502
$a
Thesis (Ph.D.)--University of Windsor (Canada), 2015.
506
$a
This item must not be sold to any third party vendors.
506
$a
This item must not be added to any third party search indexes.
520
$a
Automotive industry strives to reach an optimum level of fuel economy. This can be achieved by overcoming two impacting factors on fuel consumption: weight and friction force. This research contributes to reduce both. The proposed surface treatment can replace cylinder liners of hypoeutectic aluminum silicon alloy engine blocks with a thin layer of ceramic oxide composed of alpha and gamma phases of Al2O3 and mullite. The coatings are achieved in an aqueous electrolytic bath with current densities of 0.1 to 0.2 A/cm2.
520
$a
Coatings produced in silicate based solutions have shown good adaptability to the counter surface with an average 0.12 coefficient of friction. Coatings produced in phosphate and aluminate solution have shown signs of delamination, and excessive porosity and roughness respectively. Coatings produced under Bipolar Pulsed Direct Current mode has up to 12% higher hardness values compared to unipolar coatings. For each increment of 0.2 A/cm2 current density, there is a 30% of increase in coating growth rate. Higher pH values of the solution creates faster growth rate up to 1.5 mu/min. These coatings are 20% more susceptible to wear. Samples treated in MoS2 solution showed 22% lower average roughness values and 37% of reduction in coefficient of friction. Mild wear scars on the piston rings were detected for the optimized coatings.
590
$a
School code: 0115.
650
4
$a
Automotive engineering.
$3
2181195
650
4
$a
Materials science.
$3
543314
650
4
$a
Engineering.
$3
586835
690
$a
0540
690
$a
0794
690
$a
0537
710
2
$a
University of Windsor (Canada).
$b
Engineering Materials.
$3
2094256
773
0
$t
Dissertation Abstracts International
$g
76-10B(E).
790
$a
0115
791
$a
Ph.D.
792
$a
2015
793
$a
English
856
4 0
$u
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3706512
筆 0 讀者評論
館藏地:
全部
電子資源
出版年:
卷號:
館藏
1 筆 • 頁數 1 •
1
條碼號
典藏地名稱
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
W9296572
電子資源
11.線上閱覽_V
電子書
EB
一般使用(Normal)
在架
0
1 筆 • 頁數 1 •
1
多媒體
評論
新增評論
分享你的心得
Export
取書館
處理中
...
變更密碼
登入