Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments./
作者:	Zhang, Ying.
面頁冊數:	238 p.
附註:	Source: Masters Abstracts International, Volume: 46-04, page: 2267.
Contained By:	Masters Abstracts International46-04.
標題:	Engineering, Materials Science. -
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=MR35051
ISBN:	9780494350515

Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments.
Zhang, Ying.

Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments. - 238 p.

Source: Masters Abstracts International, Volume: 46-04, page: 2267.

Thesis (M.A.Sc.)--University of Windsor (Canada), 2007.

This thesis investigates the adhesion, friction and wear behaviour of diamond-like carbon (DLC) coatings and boron carbide (B4C) coatings. Both temperature and environmental stability of these coatings were investigated. Pin-on-disc tests against a 319 Al alloy revealed that tungsten carbide (WC) doped hydrogenated DLC coatings displayed lower coefficient of friction (COF) and wear rates than monolithic nonhydrogenated DLC coatings. WC-DLC coatings with a top layer of DLC (DLC/WC-DLC) withstood higher temperatures than WC-DLC coatings. Aluminum adhesion with the WC-DLC and DLC/WC-DLC coatings was observed at 300 and 350°C, respectively. B4C coatings exhibited higher COF and more aluminum adhesion under all test conditions. While testing under the N2 atmosphere reduced COF values for all the coatings, the humidity level of the test environment exerted various influence on each coating. The mechanisms of adhesion, friction and wear of the tribosystems were discussed based on the Al alloy-coating interactions under specific test conditions.

ISBN: 9780494350515Subjects--Topical Terms:

1017759
Engineering, Materials Science.

Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments.
LDR:01900nmm 2200241 a 45 001 891330
005 20101111
008 101111s2007 ||||||||||||||||| ||eng d
020 $a 9780494350515
035 $a (UMI)AAIMR35051
035 $a AAIMR35051
040 $a UMI $c UMI
100 1 $a Zhang, Ying. $3 1035770
245 1 0 $a Tribological properties of diamond-like carbon and boron carbide coatings against aluminum: Adhesion & friction at different temperatures and environments.
300 $a 238 p.
500 $a Source: Masters Abstracts International, Volume: 46-04, page: 2267.
502 $a Thesis (M.A.Sc.)--University of Windsor (Canada), 2007.
520 $a This thesis investigates the adhesion, friction and wear behaviour of diamond-like carbon (DLC) coatings and boron carbide (B4C) coatings. Both temperature and environmental stability of these coatings were investigated. Pin-on-disc tests against a 319 Al alloy revealed that tungsten carbide (WC) doped hydrogenated DLC coatings displayed lower coefficient of friction (COF) and wear rates than monolithic nonhydrogenated DLC coatings. WC-DLC coatings with a top layer of DLC (DLC/WC-DLC) withstood higher temperatures than WC-DLC coatings. Aluminum adhesion with the WC-DLC and DLC/WC-DLC coatings was observed at 300 and 350°C, respectively. B4C coatings exhibited higher COF and more aluminum adhesion under all test conditions. While testing under the N2 atmosphere reduced COF values for all the coatings, the humidity level of the test environment exerted various influence on each coating. The mechanisms of adhesion, friction and wear of the tribosystems were discussed based on the Al alloy-coating interactions under specific test conditions.
590 $a School code: 0115.
650 4 $a Engineering, Materials Science. $3 1017759
690 $a 0794
710 2 $a University of Windsor (Canada). $3 1018526
773 0 $t Masters Abstracts International $g 46-04.
790 $a 0115
791 $a M.A.Sc.
792 $a 2007
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=MR35051