Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment./
作者:	Zhang, Rui.
出版者:	Ann Arbor : ProQuest Dissertations & Theses, : 2021,
面頁冊數:	265 p.
附註:	Source: Dissertations Abstracts International, Volume: 83-01, Section: B.
Contained By:	Dissertations Abstracts International83-01B.
標題:	Mechanical engineering. -
電子資源:	https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=28416273
ISBN:	9798516960925

Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment.
Zhang, Rui.

Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment. - Ann Arbor : ProQuest Dissertations & Theses, 2021 - 265 p.

Source: Dissertations Abstracts International, Volume: 83-01, Section: B.

Thesis (Ph.D.)--Syracuse University, 2021.

This item must not be sold to any third party vendors.

The effects of moisture content, temperature, and pollutant mixture on atmospheric corrosion of copper and silver were investigated by exposing test specimens to different environmental conditions, followed by surface characterization using the coulometric reduction, Scanning Electron Microscopy, and Energy Dispersive Spectrometry (SEM/EDS). Printed circuit board test cards (PCBs) with bare copper were also used to investigate the effects of voltage bias on the PCBs on the corrosion rate. The test specimens were exposed to mixed flowing gases (MFG) environment with eight different combinations of the following five pollutants at the fixed concentration levels: 60 ppb O3, 80 ppb NO2, 40 ppb SO2, 2 ppb Cl2, and 10 ppb H2S. Temperature and relative humidity (RH) were varied from a reference condition (21°C and 50% RH which is within the current ASHRAE-recommended thermal envelope) to a higher value (28°C, 70% RH, or 80% RH) to increase the moisture content of the test environment. Test results revealed the dominating effect of Cl2 on copper corrosion and that of H2S on silver corrosion. Increasing the moisture content at 21°C caused more severe corrosion of copper when Cl2 was present, but not for silver. When the temperature was increased from 21°C to 28°C at 50% RH, it reduced the corrosion of copper, but not for silver. Voltage-biased PCBs had less effect on corrosion than PCBs without the voltage bias. A mechanistic model based on the multi-ion transport and chemical reactions was also proposed to predict the corrosion of copper due to Cl2-containing pollutant mixtures. The model's prediction of the effects of temperature and RH agreed well with the experimental results. These findings provided the basis for possible expansion of the ASHRAE-recommended thermal envelope for data centers when Cl2 and H2S are not present and limiting the thermal envelope when Cl2 or H2S is present. They also improved the understanding of the corrosion mechanisms for the copper when Cl2 is present in the data center environment.

ISBN: 9798516960925Subjects--Topical Terms:

649730
Mechanical engineering.

Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment.
LDR:03126nmm a2200325 4500 001 2281617
005 20210920103559.5
008 220723s2021 ||||||||||||||||| ||eng d
020 $a 9798516960925
035 $a (MiAaPQ)AAI28416273
035 $a AAI28416273
040 $a MiAaPQ $c MiAaPQ
100 1 $a Zhang, Rui. $3 1273551
245 1 0 $a Effects of Air Pollution, Temperature and Moisture Content on Copper and Silver Corrosions and the Reliability of Data Center Equipment.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2021
300 $a 265 p.
500 $a Source: Dissertations Abstracts International, Volume: 83-01, Section: B.
500 $a Advisor: Zhang, Jianshun.
502 $a Thesis (Ph.D.)--Syracuse University, 2021.
506 $a This item must not be sold to any third party vendors.
520 $a The effects of moisture content, temperature, and pollutant mixture on atmospheric corrosion of copper and silver were investigated by exposing test specimens to different environmental conditions, followed by surface characterization using the coulometric reduction, Scanning Electron Microscopy, and Energy Dispersive Spectrometry (SEM/EDS). Printed circuit board test cards (PCBs) with bare copper were also used to investigate the effects of voltage bias on the PCBs on the corrosion rate. The test specimens were exposed to mixed flowing gases (MFG) environment with eight different combinations of the following five pollutants at the fixed concentration levels: 60 ppb O3, 80 ppb NO2, 40 ppb SO2, 2 ppb Cl2, and 10 ppb H2S. Temperature and relative humidity (RH) were varied from a reference condition (21°C and 50% RH which is within the current ASHRAE-recommended thermal envelope) to a higher value (28°C, 70% RH, or 80% RH) to increase the moisture content of the test environment. Test results revealed the dominating effect of Cl2 on copper corrosion and that of H2S on silver corrosion. Increasing the moisture content at 21°C caused more severe corrosion of copper when Cl2 was present, but not for silver. When the temperature was increased from 21°C to 28°C at 50% RH, it reduced the corrosion of copper, but not for silver. Voltage-biased PCBs had less effect on corrosion than PCBs without the voltage bias. A mechanistic model based on the multi-ion transport and chemical reactions was also proposed to predict the corrosion of copper due to Cl2-containing pollutant mixtures. The model's prediction of the effects of temperature and RH agreed well with the experimental results. These findings provided the basis for possible expansion of the ASHRAE-recommended thermal envelope for data centers when Cl2 and H2S are not present and limiting the thermal envelope when Cl2 or H2S is present. They also improved the understanding of the corrosion mechanisms for the copper when Cl2 is present in the data center environment.
590 $a School code: 0659.
650 4 $a Mechanical engineering. $3 649730
650 4 $a Chemistry. $3 516420
650 4 $a Materials science. $3 543314
650 4 $a Laboratories. $3 531588
650 4 $a Air filters. $3 3398351
650 4 $a Pollutants. $3 551065
650 4 $a Humidity. $3 3559498
650 4 $a Trends. $3 3560051
650 4 $a Printed circuit boards. $3 3560292
650 4 $a Discount coupons. $3 3560293
650 4 $a Silver. $3 2006426
650 4 $a Color. $3 533870
650 4 $a Atmospheric corrosion. $3 3560294
650 4 $a Air pollution. $3 888377
650 4 $a Energy consumption. $3 631630
650 4 $a Scanning electron microscopy. $3 551366
650 4 $a Corrosion tests. $3 3560295
650 4 $a Electrical currents. $3 3560296
650 4 $a Research methodology. $3 3559994
650 4 $a Cooling. $3 1457878
650 4 $a Gases. $3 559387
650 4 $a Environmental conditions. $3 3550086
650 4 $a Temperature effects. $3 3560297
650 4 $a Experiments. $3 525909
650 4 $a HVAC. $3 3555644
650 4 $a Information technology. $3 532993
650 4 $a Geometry. $3 517251
690 $a 0548
690 $a 0794
690 $a 0485
690 $a 0489
710 2 $a Syracuse University. $b Mechanical and Aerospace Engineering. $3 2104096
773 0 $t Dissertations Abstracts International $g 83-01B.
790 $a 0659
791 $a Ph.D.
792 $a 2021
793 $a English
856 4 0 $u https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=28416273