Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication.
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication./
作者:
Wang, Yanjie.
面頁冊數:
64 p.
附註:
Source: Dissertation Abstracts International, Volume: 74-03(E), Section: B.
Contained By:
Dissertation Abstracts International74-03B(E).
標題:
Engineering, Electronics and Electrical. -
電子資源:
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3532480
ISBN:
9781267753908
Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication.
Wang, Yanjie.
Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication.
- 64 p.
Source: Dissertation Abstracts International, Volume: 74-03(E), Section: B.
Thesis (Ph.D.)--University of California, Los Angeles, 2012.
This item is not available from ProQuest Dissertations & Theses.
As the first free-standing 2D crystal, graphene was discovered in 2004 by Andre Geim and Kostya Novoselov of Manchester University using a technique called micromechanical cleavage [1]. Since then, graphene has attracted vast interest in solid-state physics, materials science, nanoelectronics and bioscience. Graphene is considered as a promising electronic material in post-silicon electronics due to its potential compatibility with planar technology while maintaining much of the transport advantages of carbon nanotubes (CNTs). Graphene transistors have behave high intrinsic carrier mobility (>10,000 cm 2/V•s) [2], large saturation velocity (5.5x107 cm/s)[3], and high on-state current density (>3 A/mm)[4, 5],which makes it tobe a promising candidate for high-frequency devices. Graphene-based field-effect transistors (FETs) with a cutoff frequency of 300 GHz[5] has been achieved on exfoliated graphene. For top gate graphene FETs, J. S. Moon et al. reported epitaxial graphene FETs on SiC with a mobility of 6,000 cm2/V•s[4]; Xuesong Li et al. reported extracted mobility of 4,050 cm2/V•s with CVD graphene on Cu[6]; Lei Liao et al. reported extracted mobility of 23,600 cm2/V•s with mechanical exfoliated graphene[7].
ISBN: 9781267753908Subjects--Topical Terms:
626636
Engineering, Electronics and Electrical.
Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication.
LDR
:04710nmm a2200349 4500
001
2056953
005
20150630121426.5
008
170521s2012 ||||||||||||||||| ||eng d
020
$a
9781267753908
035
$a
(MiAaPQ)AAI3532480
035
$a
AAI3532480
040
$a
MiAaPQ
$c
MiAaPQ
100
1
$a
Wang, Yanjie.
$3
3170747
245
1 0
$a
Scalable Synthesis of Graphene on Patterned Nickel and Transistor Fabrication.
300
$a
64 p.
500
$a
Source: Dissertation Abstracts International, Volume: 74-03(E), Section: B.
500
$a
Adviser: James C. S. Woo.
502
$a
Thesis (Ph.D.)--University of California, Los Angeles, 2012.
506
$a
This item is not available from ProQuest Dissertations & Theses.
506
$a
This item must not be sold to any third party vendors.
506
$a
This item must not be added to any third party search indexes.
520
$a
As the first free-standing 2D crystal, graphene was discovered in 2004 by Andre Geim and Kostya Novoselov of Manchester University using a technique called micromechanical cleavage [1]. Since then, graphene has attracted vast interest in solid-state physics, materials science, nanoelectronics and bioscience. Graphene is considered as a promising electronic material in post-silicon electronics due to its potential compatibility with planar technology while maintaining much of the transport advantages of carbon nanotubes (CNTs). Graphene transistors have behave high intrinsic carrier mobility (>10,000 cm 2/V•s) [2], large saturation velocity (5.5x107 cm/s)[3], and high on-state current density (>3 A/mm)[4, 5],which makes it tobe a promising candidate for high-frequency devices. Graphene-based field-effect transistors (FETs) with a cutoff frequency of 300 GHz[5] has been achieved on exfoliated graphene. For top gate graphene FETs, J. S. Moon et al. reported epitaxial graphene FETs on SiC with a mobility of 6,000 cm2/V•s[4]; Xuesong Li et al. reported extracted mobility of 4,050 cm2/V•s with CVD graphene on Cu[6]; Lei Liao et al. reported extracted mobility of 23,600 cm2/V•s with mechanical exfoliated graphene[7].
520
$a
However, mass production of high quality graphene on insulator substrate is a bottleneck for the practical application of graphene as an electronic material. Mechanical exfoliation and wet chemistry-based approaches cannot increase to large-scale and well-ordered graphene. SiC epitaxial has the prospect of producing graphene over an entire wafer, but it requires expensive substrate. For CVD graphene on metals, PDMS or PMMA transfer is typically used, resulting in contamination between graphene and the new substrate, ultimately degrading mobility. For high frequency application of graphene FETs, low parasitic capacitance, small series resistance and high mobility are essential elements. Most of the graphene FETs with self-aligned structure published to date [5, 8, 9] are with top gate structure. For the top gated graphene FETs, the gate and source/drain are on the same side of graphene, which may cause large fringing capacitance especially for short channel devices. Also the way to make the source/drain self-aligned will restrict the contact metal thickness to around 10nm, which will address the reliability issue of the contact.
520
$a
With the goal of overcoming these difficulties, this project investigates an approach to mass product high quality graphene and corresponding transistors fabrication. Ni dots with single or few grains were achieved by annealing. Single layer graphene with good crystalline quality has been grown on Ni dots. The patterned graphene films were transferred to insulating substrates by wafer bonding and etch back technique, which gives zero mis-alignment, low contamination as well as high yield(>90%). Graphene based field-effect transistors with self-aligned buried gate were fabricated with this method. The field effective mobility of 6,100 cm2/V•s and 24,000 cm 2/V•s was achieved before and after subtraction of contact resistance, respectively. The extracted source/drain contact resistivity between Ti/Pd/Au and graphene was found to be in the order of 10-7 O cm 2. The channel length was scaled down to 100 run, high transconductance (438mS/mm) was maintained in 100nm channel length devices. These results demonstrate the potential of this method as a candidate for mass production of graphene transistors for RF application.
590
$a
School code: 0031.
650
4
$a
Engineering, Electronics and Electrical.
$3
626636
650
4
$a
Physics, Solid State.
$3
1669244
650
4
$a
Engineering, Materials Science.
$3
1017759
690
$a
0544
690
$a
0600
690
$a
0794
710
2
$a
University of California, Los Angeles.
$b
Electrical Engineering.
$3
2094815
773
0
$t
Dissertation Abstracts International
$g
74-03B(E).
790
$a
0031
791
$a
Ph.D.
792
$a
2012
793
$a
English
856
4 0
$u
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3532480
筆 0 讀者評論
館藏地:
全部
電子資源
出版年:
卷號:
館藏
1 筆 • 頁數 1 •
1
條碼號
典藏地名稱
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
W9289457
電子資源
11.線上閱覽_V
電子書
EB
一般使用(Normal)
在架
0
1 筆 • 頁數 1 •
1
多媒體
評論
新增評論
分享你的心得
Export
取書館
處理中
...
變更密碼
登入