Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth.

Record Type:	Language materials, printed : Monograph/item
Title/Author:	Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth./
Author:	Marx, Brian M.
Description:	147 p.
Notes:	Source: Dissertation Abstracts International, Volume: 67-08, Section: B, page: 4648.
Contained By:	Dissertation Abstracts International67-08B.
Subject:	Engineering, Metallurgy. -
Online resource:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3229432
ISBN:	9780542810015

Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth.
Marx, Brian M.

Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth. - 147 p.

Source: Dissertation Abstracts International, Volume: 67-08, Section: B, page: 4648.

Thesis (Ph.D.)--The Pennsylvania State University, 2006.

In this thesis the passive oxide film formed on iron is studied using many experimental techniques in order to aid in the refinement of a Point Defect Model (PDM), which is capable of predicting and quantifying damage due to the general corrosion of iron. Many older electrochemical methods, like Mott-Schottky analysis, are incorporated with more modern techniques, such as scanning wavelength ellipsometry, electrochemical impedance spectroscopy, and XPS to probe the oxide film.

ISBN: 9780542810015Subjects--Topical Terms:

1023648
Engineering, Metallurgy.

Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth.
LDR:02902nam 2200301 4500 001 1395904
005 20110527105417.5
008 130515s2006 ||||||||||||||||| ||eng d
020 $a 9780542810015
035 $a (UMI)AAI3229432
035 $a AAI3229432
040 $a UMI $c UMI
100 1 $a Marx, Brian M. $3 1674644
245 1 0 $a Exploring the mechanisms of passivity on iron: Experimental methods for characterizing and developing models to describe nano-oxide growth.
300 $a 147 p.
500 $a Source: Dissertation Abstracts International, Volume: 67-08, Section: B, page: 4648.
500 $a Adviser: D. D. Macdonald.
502 $a Thesis (Ph.D.)--The Pennsylvania State University, 2006.
520 $a In this thesis the passive oxide film formed on iron is studied using many experimental techniques in order to aid in the refinement of a Point Defect Model (PDM), which is capable of predicting and quantifying damage due to the general corrosion of iron. Many older electrochemical methods, like Mott-Schottky analysis, are incorporated with more modern techniques, such as scanning wavelength ellipsometry, electrochemical impedance spectroscopy, and XPS to probe the oxide film.
520 $a Ellipsometry is used to make in-situ thickness measurements that are performed in unison with potentiostatic and impedance experiments. XPS analysis is used to determine the concentrations of Fe2+ and Fe 3+ present in the oxide film formed on iron. The information obtained is used to derive a PDM containing only oxygen vacancies. In addition, a new idea is proposed concerning three distinct regions over the passive range exhibited by iron in a borate buffer solution. Each region corresponds to a change in the electronic behavior of the film as evidenced by basic Mott-Schottky analysis. It is proposed that these different regions represent phase changes for the film.
520 $a Finally, the oxygen vacancy PDM is applied to implicitly determine if the major defects in the iron oxide film are oxide vacancies. The PDM is also fitted to the experimental data to yield the kinetic parameters and to make predictions concerning the steady-state thickness and current. A Warburg impedance is used in the fitting to obtain diffusivity data for the defects. The kinetic parameters are generated as both a function of formation potential and temperature. A PDM, containing only oxygen vacancies, does not fit the data. Therefore, iron interstitials were added to the model, which yielded good fits to the data. A discussion is provided as to the interpretation of the results and the viability of applying the PDM to the iron system.
590 $a School code: 0176.
650 4 $a Engineering, Metallurgy. $3 1023648
650 4 $a Engineering, Materials Science. $3 1017759
690 $a 0743
690 $a 0794
710 2 $a The Pennsylvania State University. $3 699896
773 0 $t Dissertation Abstracts International $g 67-08B.
790 1 0 $a Macdonald, D. D., $e advisor
790 $a 0176
791 $a Ph.D.
792 $a 2006
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3229432