Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance.
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance./
作者:
Cui, Yuchi.
出版者:
Ann Arbor : ProQuest Dissertations & Theses, : 2020,
面頁冊數:
147 p.
附註:
Source: Dissertations Abstracts International, Volume: 81-11, Section: B.
Contained By:
Dissertations Abstracts International81-11B.
標題:
Engineering. -
電子資源:
https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=28006491
ISBN:
9798643183808
Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance.
Cui, Yuchi.
Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance.
- Ann Arbor : ProQuest Dissertations & Theses, 2020 - 147 p.
Source: Dissertations Abstracts International, Volume: 81-11, Section: B.
Thesis (Ph.D.)--University of Michigan, 2020.
This item must not be sold to any third party vendors.
In metallic materials, flow strength and plasticity are typically mutually exclusive and there is a pressing demand for the design of nanostructures that will solve the strength-deformability trade-off. Metallic nanocomposites (MNC) have been studied to exhibit high uniaxial strengths in the form of multilayers, with a general "smaller is stronger" trend in terms of the layer thickness. However, localized deformation in the form of shear bands results in limited deformability of these multilayer MNCs. It was hypothesized that, through high-temperature co-sputtering of two immiscible metals, novel morphological designs at nano-scale, including bicontinuous intertwined structure and heterogeneous structures where larger crystalline phases present, will be produced and they will promote plasticity while maintaining high strength of the nanocomposite. Cu-Mo nanocomposites with various morphologies have been prepared via high-temperature co-sputtering, including vertical concentration modulation (VCM), lateral concentration modulation (LCM), random concentration modulation (RCM) structures and a hierarchical "composite of composites" architecture where sub-micron scale Cu-rich islands containing Mo nano-precipitates are dispersed in a matrix of phase-separated Cu-Mo with nanoscale ligaments. Through advanced electron microscopy characterizations and in situ nanomechanical testing, deformation mechanisms of these nanocomposites have been studied and related to the nanostructures. High flow stress over 2 GPa were measured from all these nanocomposites. It has been discovered that the VCM and LCM structures lack uniform deformability due to the formation of localized shear bands or kink bands. On the other hand, uniform deformability was observed in the rest two structures: the RCM or bicontinuous intertwined structure and the hierarchical structures. The complexity in the RCM structure poses geometric constraint on the softer Cu phase, promoting strain hardening and thus increasing the strength of the material. The tortuous interfaces effectively block the propagation of local strain concentration, resulting in the uniform deformation. In the hierarchical structure, the stronger matrix provides strength while the larger grain-size Cu-rich island promote deformability. The hierarchical structure has also been shown to have significant higher fracture resistance compared to the multilayers. These findings will provide insights to the understanding of interface microstructure-induced plasticity and fracture toughness enhancement in metallic materials and thus facilitate the design of metallic nanocomposites for advanced structural applications.
ISBN: 9798643183808Subjects--Topical Terms:
586835
Engineering.
Subjects--Index Terms:
Nanomechanics
Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance.
LDR
:03992nmm a2200397 4500
001
2275293
005
20201202130455.5
008
220723s2020 ||||||||||||||||| ||eng d
020
$a
9798643183808
035
$a
(MiAaPQ)AAI28006491
035
$a
(MiAaPQ)umichrackham003036
035
$a
AAI28006491
040
$a
MiAaPQ
$c
MiAaPQ
100
1
$a
Cui, Yuchi.
$3
3553536
245
1 0
$a
Design of Metallic Nanocomposites for High-Strength, Plasticity and Fracture Resistance.
260
1
$a
Ann Arbor :
$b
ProQuest Dissertations & Theses,
$c
2020
300
$a
147 p.
500
$a
Source: Dissertations Abstracts International, Volume: 81-11, Section: B.
500
$a
Advisor: Misra, Amit.
502
$a
Thesis (Ph.D.)--University of Michigan, 2020.
506
$a
This item must not be sold to any third party vendors.
506
$a
This item must not be added to any third party search indexes.
520
$a
In metallic materials, flow strength and plasticity are typically mutually exclusive and there is a pressing demand for the design of nanostructures that will solve the strength-deformability trade-off. Metallic nanocomposites (MNC) have been studied to exhibit high uniaxial strengths in the form of multilayers, with a general "smaller is stronger" trend in terms of the layer thickness. However, localized deformation in the form of shear bands results in limited deformability of these multilayer MNCs. It was hypothesized that, through high-temperature co-sputtering of two immiscible metals, novel morphological designs at nano-scale, including bicontinuous intertwined structure and heterogeneous structures where larger crystalline phases present, will be produced and they will promote plasticity while maintaining high strength of the nanocomposite. Cu-Mo nanocomposites with various morphologies have been prepared via high-temperature co-sputtering, including vertical concentration modulation (VCM), lateral concentration modulation (LCM), random concentration modulation (RCM) structures and a hierarchical "composite of composites" architecture where sub-micron scale Cu-rich islands containing Mo nano-precipitates are dispersed in a matrix of phase-separated Cu-Mo with nanoscale ligaments. Through advanced electron microscopy characterizations and in situ nanomechanical testing, deformation mechanisms of these nanocomposites have been studied and related to the nanostructures. High flow stress over 2 GPa were measured from all these nanocomposites. It has been discovered that the VCM and LCM structures lack uniform deformability due to the formation of localized shear bands or kink bands. On the other hand, uniform deformability was observed in the rest two structures: the RCM or bicontinuous intertwined structure and the hierarchical structures. The complexity in the RCM structure poses geometric constraint on the softer Cu phase, promoting strain hardening and thus increasing the strength of the material. The tortuous interfaces effectively block the propagation of local strain concentration, resulting in the uniform deformation. In the hierarchical structure, the stronger matrix provides strength while the larger grain-size Cu-rich island promote deformability. The hierarchical structure has also been shown to have significant higher fracture resistance compared to the multilayers. These findings will provide insights to the understanding of interface microstructure-induced plasticity and fracture toughness enhancement in metallic materials and thus facilitate the design of metallic nanocomposites for advanced structural applications.
590
$a
School code: 0127.
650
4
$a
Engineering.
$3
586835
650
4
$a
Materials science.
$3
543314
650
4
$a
Mechanics.
$3
525881
653
$a
Nanomechanics
653
$a
metallic nanocomposite
653
$a
extreme mechanics
653
$a
in situ characterization
653
$a
electron microscopy
690
$a
0537
690
$a
0794
690
$a
0346
710
2
$a
University of Michigan.
$b
Materials Science and Engineering.
$3
3281089
773
0
$t
Dissertations Abstracts International
$g
81-11B.
790
$a
0127
791
$a
Ph.D.
792
$a
2020
793
$a
English
856
4 0
$u
https://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=28006491
筆 0 讀者評論
館藏地:
全部
電子資源
出版年:
卷號:
館藏
1 筆 • 頁數 1 •
1
條碼號
典藏地名稱
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
W9427026
電子資源
11.線上閱覽_V
電子書
EB
一般使用(Normal)
在架
0
1 筆 • 頁數 1 •
1
多媒體
評論
新增評論
分享你的心得
Export
取書館
處理中
...
變更密碼
登入