Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing.
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing./
作者:
Salem Mohamed, Serageldin.
出版者:
Ann Arbor : ProQuest Dissertations & Theses, : 2018,
面頁冊數:
217 p.
附註:
Source: Dissertation Abstracts International, Volume: 79-12(E), Section: B.
Contained By:
Dissertation Abstracts International79-12B(E).
標題:
Engineering. -
電子資源:
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10841155
ISBN:
9780438204867
Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing.
Salem Mohamed, Serageldin.
Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing.
- Ann Arbor : ProQuest Dissertations & Theses, 2018 - 217 p.
Source: Dissertation Abstracts International, Volume: 79-12(E), Section: B.
Thesis (Ph.D.)--Universite du Quebec a Chicoutimi (Canada), 2018.
Using light-weight materials have become an important factor in the automotive industry due to stringent government regulations on fuel consumption. Aluminum alloys are 65% lighter than cast iron enabling significant weight reduction. However, there are several significant challenges associated to the use of hypoeutectic Al-Si alloys in engine block applications. This dissertation investigated the factors influencing the development of residual stresses in I-4 and V-6 engine blocks due to different heat treatments and introducing sub-zero treatment as a mean for reducing residual stresses.
ISBN: 9780438204867Subjects--Topical Terms:
586835
Engineering.
Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing.
LDR
:04074nmm a2200349 4500
001
2202015
005
20190503113355.5
008
201008s2018 ||||||||||||||||| ||eng d
020
$a
9780438204867
035
$a
(MiAaPQ)AAI10841155
035
$a
(MiAaPQ)uqac:10470
035
$a
AAI10841155
040
$a
MiAaPQ
$c
MiAaPQ
100
1
$a
Salem Mohamed, Serageldin.
$3
3428769
245
1 0
$a
Effects of Metallurgical Parameters on the Development of Residual Stresses in Al-Si Alloys Used in Engine Block Manufacturing.
260
1
$a
Ann Arbor :
$b
ProQuest Dissertations & Theses,
$c
2018
300
$a
217 p.
500
$a
Source: Dissertation Abstracts International, Volume: 79-12(E), Section: B.
500
$a
Adviser: Fawzy Hosny Samuel.
502
$a
Thesis (Ph.D.)--Universite du Quebec a Chicoutimi (Canada), 2018.
520
$a
Using light-weight materials have become an important factor in the automotive industry due to stringent government regulations on fuel consumption. Aluminum alloys are 65% lighter than cast iron enabling significant weight reduction. However, there are several significant challenges associated to the use of hypoeutectic Al-Si alloys in engine block applications. This dissertation investigated the factors influencing the development of residual stresses in I-4 and V-6 engine blocks due to different heat treatments and introducing sub-zero treatment as a mean for reducing residual stresses.
520
$a
The initial section of this thesis explores the development of residual stresses with different casting parameters in A356.1 and B319.1 castings with simple geometries. This analysis involved measurement of tensile properties, microstructural analysis, and residual stress measurement using sectioning technique. The casting parameters include cooling rate, quenching media, aging time and aging temperature. The second phase of this study will investigate the development of residual stress in castings, with more complex shape such as in I-4 and V-6 engine blocks with cast-in gray iron liners, with different heat treatment parameters and sub-zero treatment.
520
$a
An analysis of result shows that higher strength materials, as in B319.1 alloy, produce higher residual stresses compared to material with lower strength, as in the case of A356.1. The results also show that there is direct proportionality between ultimate tensile stresses (UTS) and residual stresses (RS) with quenching rate. The residual stresses were found to gradually decrease with decreasing cooling/quenching rates of the quenching medium. The quenching process develops the highest residual stresses, where quenching in cold water develops the highest, and air cooling the lowest, residual stresses. The relaxation of residual stresses is significantly dependent on aging temperature and proceeds smoothly with the increase in aging time. Finally, significant increase in the residual stresses is observed in specimens with low SDAS, as in the L-shaped casting (high solidification rate), while lower residual stresses are measured in specimens with high SDAS, as in the block casting (low solidification rate).
520
$a
For I4 and V-6 engine blocks, the results suggest that there is refinement in microstructure due to increases cooling rate along the cylinder. The developed residual stresses were found to be tensile for both I-4 and V-6 engine blocks. Furthermore, the variation in the developed residual stresses was found to be insignificant. The results also indicate that air cooling produced the highest residual stresses compared to warm water and cold-water quenching. Solution heat treatment and freezing led to maximum amount of residual stress relaxation where 50% of the residual stresses were reduced after SHT step Aging time and aging temperature is directly proportional to the residual stresses relaxation.
590
$a
School code: 0862.
650
4
$a
Engineering.
$3
586835
650
4
$a
Automotive engineering.
$3
2181195
650
4
$a
Materials science.
$3
543314
690
$a
0537
690
$a
0540
690
$a
0794
710
2
$a
Universite du Quebec a Chicoutimi (Canada).
$b
Sciences appliquees.
$3
3348137
773
0
$t
Dissertation Abstracts International
$g
79-12B(E).
790
$a
0862
791
$a
Ph.D.
792
$a
2018
793
$a
English
856
4 0
$u
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10841155
筆 0 讀者評論
館藏地:
全部
電子資源
出版年:
卷號:
館藏
1 筆 • 頁數 1 •
1
條碼號
典藏地名稱
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
W9378564
電子資源
11.線上閱覽_V
電子書
EB
一般使用(Normal)
在架
0
1 筆 • 頁數 1 •
1
多媒體
評論
新增評論
分享你的心得
Export
取書館
處理中
...
變更密碼
登入