Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application./
作者:	Zhao, Shan.
出版者:	Ann Arbor : ProQuest Dissertations & Theses, : 2017,
面頁冊數:	128 p.
附註:	Source: Dissertation Abstracts International, Volume: 78-10(E), Section: B.
Contained By:	Dissertation Abstracts International78-10B(E).
標題:	Materials science. -
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10266745
ISBN:	9781369820447

Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application.
Zhao, Shan.

Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application. - Ann Arbor : ProQuest Dissertations & Theses, 2017 - 128 p.

Source: Dissertation Abstracts International, Volume: 78-10(E), Section: B.

Thesis (Ph.D.)--Michigan Technological University, 2017.

Zinc has begun to be studied as a bio-degradable material in recent years due to its excellent corrosion rate and optimal biocompatibility. Unfortunately, pure Zn's intrinsic ultimate tensile strength (UTS; below 120 MPa) is lower than the benchmark (about 300 MPa) for cardiovascular stent materials, raising concerns about sufficient strength to support the blood vessel. Thus, modifying pure Zn to improve its mechanical properties is an important research topic. In this dissertation project, a new Zn-Li alloy has been developed to retain the outstanding corrosion behavior from Zn while improving the mechanical characteristics and uniform biodegradation once it is implanted into the artery of Sprague-Dawley rats. The completed work includes:

ISBN: 9781369820447Subjects--Topical Terms:

543314
Materials science.

Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application.
LDR:02686nmm a2200301 4500 001 2159616
005 20180703084422.5
008 190424s2017 ||||||||||||||||| ||eng d
020 $a 9781369820447
035 $a (MiAaPQ)AAI10266745
035 $a (MiAaPQ)michigantech:11278
035 $a AAI10266745
040 $a MiAaPQ $c MiAaPQ
100 1 $a Zhao, Shan. $3 3171737
245 1 0 $a Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application.
260 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2017
300 $a 128 p.
500 $a Source: Dissertation Abstracts International, Volume: 78-10(E), Section: B.
500 $a Advisers: Jaroslaw W. Drelich; Jeremy Goldman.
502 $a Thesis (Ph.D.)--Michigan Technological University, 2017.
520 $a Zinc has begun to be studied as a bio-degradable material in recent years due to its excellent corrosion rate and optimal biocompatibility. Unfortunately, pure Zn's intrinsic ultimate tensile strength (UTS; below 120 MPa) is lower than the benchmark (about 300 MPa) for cardiovascular stent materials, raising concerns about sufficient strength to support the blood vessel. Thus, modifying pure Zn to improve its mechanical properties is an important research topic. In this dissertation project, a new Zn-Li alloy has been developed to retain the outstanding corrosion behavior from Zn while improving the mechanical characteristics and uniform biodegradation once it is implanted into the artery of Sprague-Dawley rats. The completed work includes:
520 $a Manufactured Zn-Li alloy ingots and sheets via induction vacuum casting, melt spinning, hot rolling deformation, and wire electro discharge machining (wire EDM) technique; processed alloy samples using cross sectioning, mounting, etching and polishing technique; • Characterized alloy ingots, sheets and wires using hardness and tensile test, XRD, BEI imaging, SEM, ESEM, FTIR, ICP-OES and electrochemical test; then selected the optimum composition for in vitro and in vivo experiments; • Mimicked the degradation behavior of the Zn-Li alloy in vitro using simulated body fluid (SBF) and explored the relations between corrosion rate, corrosion products and surface morphology with changing compositions; • Explanted the Zn-Li alloy wire in abdominal aorta of rat over 12 months and studied its degradation mechanism, rate of bioabsorption, cytotoxicity and corrosion product migration from histological analysis.
590 $a School code: 0129.
650 4 $a Materials science. $3 543314
690 $a 0794
710 2 $a Michigan Technological University. $b Materials Science and Engineering. $3 3281122
773 0 $t Dissertation Abstracts International $g 78-10B(E).
790 $a 0129
791 $a Ph.D.
792 $a 2017
793 $a English
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10266745