Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions.
紀錄類型:
書目-電子資源 : Monograph/item
正題名/作者:
Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions./
作者:
Kahkonen, Joonas.
面頁冊數:
194 p.
附註:
Source: Masters Abstracts International, Volume: 55-04.
Contained By:
Masters Abstracts International55-04(E).
標題:
Materials science. -
電子資源:
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10110739
ISBN:
9781339739847
Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions.
Kahkonen, Joonas.
Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions.
- 194 p.
Source: Masters Abstracts International, Volume: 55-04.
Thesis (M.S.)--Colorado School of Mines, 2016.
In order to produce passenger vehicles with improved fuel economy and increased passenger safety, car manufacturers are in need of steels with enhanced strength levels and good formability. Recently, promising combinations of strength and ductility have been reported for several, so-called third generation advanced high-strength steels (AHSS) and quenching and partitioning (Q&P) steels are increasingly being recognized as a promising third generation AHSS candidate.
ISBN: 9781339739847Subjects--Topical Terms:
543314
Materials science.
Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions.
LDR
:03890nmm a2200313 4500
001
2071281
005
20160708094620.5
008
170521s2016 ||||||||||||||||| ||eng d
020
$a
9781339739847
035
$a
(MiAaPQ)AAI10110739
035
$a
AAI10110739
040
$a
MiAaPQ
$c
MiAaPQ
100
1
$a
Kahkonen, Joonas.
$3
3186411
245
1 0
$a
Quenching and partitioning response of carbon-manganese-silicon sheet steels containing nickel, molybdenum, aluminum and copper additions.
300
$a
194 p.
500
$a
Source: Masters Abstracts International, Volume: 55-04.
500
$a
Adviser: Emmanuel De Moor.
502
$a
Thesis (M.S.)--Colorado School of Mines, 2016.
520
$a
In order to produce passenger vehicles with improved fuel economy and increased passenger safety, car manufacturers are in need of steels with enhanced strength levels and good formability. Recently, promising combinations of strength and ductility have been reported for several, so-called third generation advanced high-strength steels (AHSS) and quenching and partitioning (Q&P) steels are increasingly being recognized as a promising third generation AHSS candidate.
520
$a
Early Q research used conventional TRIP steel chemistries and richer alloying strategies have been explored in more recent studies. However, systematic investigations of the effects of alloying elements on tensile properties and retained austenite fractions of Q&P steels are sparse. The objective of the present research was to investigate the alloying effects of carbon, manganese, molybdenum, aluminum, copper and nickel on tensile properties and microstructural evolution of Q&P heat treated sheet steels. Seven alloys were investigated with 0.3C-1.5Mn-1.5Si (wt pct) and 0.4C-1.5Mn-1.5Si alloys used to study carbon effects, a 0.3C-5Mn-1.6Si alloy to study manganese effects, 0.3C-3Mn-1.5Si-0.25Mo and 0.3C-3Mn-1.5Si-0.25Mo-0.85Al alloys to study molybdenum and aluminum effects and 0.2C-1.5Mn-1.3Si-1.5Cu and 0.2C-1.5Mn-1.3Si-1.5Cu-1.5Ni alloys to study copper and nickel effects.
520
$a
Increasing alloy carbon content was observed to mainly increase the ultimate tensile strength (UTS) up to 1865 MPa without significantly affecting total elongation (TE) levels. Increasing alloy carbon content also increased the resulting retained austenite (RA) fractions up to 22 vol pct. Measured maximum RA fractions were significantly lower than the predicted maximum RA levels in the 0.3C-1.5Mn-1.5Si and 0.4C-1.5Mn-1.5Si alloys, likely resulting from transition carbide formation. Increasing alloy manganese content increased UTS, TE and RA levels, and decreased yield strength (YS) and austenite carbon content (Cgamma) levels. Retained austenite fractions up to 28 pct and UTS levels exceeding 1500, 1600, and 1700 MPa with TE levels of 20, 17 and 12 pct respectively were measured for the 0.3C-5Mn-1.6Si alloy.
520
$a
Molybdenum and aluminum additions to a 0.3C-3Mn-1.5Si alloy were not observed to significantly affect the resulting tensile properties at a partitioning temperature of 400 °C. Partitioning at 450 °C increased the TE levels of the 0.3C-3Mn-1.5Si-0.25Mo-0.85Al alloy and decreased the TE levels of the 0.3C-3Mn-1.5Si-0.25Mo alloy while similar UTS levels were measured in both alloys. The aluminum addition potentially increased strain hardening. RA fractions were observed to be close to predicted levels in both alloys. Copper and nickel additions were not observed to increase the resulting maximum UTS˙TE levels. Copper and nickel additions increased RA levels and the measured RA levels were observed to be close to the predicted values.
590
$a
School code: 0052.
650
4
$a
Materials science.
$3
543314
650
4
$a
Automotive engineering.
$3
2181195
690
$a
0794
690
$a
0540
710
2
$a
Colorado School of Mines.
$b
Metallurgical and Materials Engineering.
$3
2093645
773
0
$t
Masters Abstracts International
$g
55-04(E).
790
$a
0052
791
$a
M.S.
792
$a
2016
793
$a
English
856
4 0
$u
http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10110739
筆 0 讀者評論
館藏地:
全部
電子資源
出版年:
卷號:
館藏
1 筆 • 頁數 1 •
1
條碼號
典藏地名稱
館藏流通類別
資料類型
索書號
使用類型
借閱狀態
預約狀態
備註欄
附件
W9304149
電子資源
11.線上閱覽_V
電子書
EB
一般使用(Normal)
在架
0
1 筆 • 頁數 1 •
1
多媒體
評論
新增評論
分享你的心得
Export
取書館
處理中
...
變更密碼
登入