Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques./
作者:	Ebrahimpour, Omid.
面頁冊數:	203 p.
附註:	Source: Dissertation Abstracts International, Volume: 75-12(E), Section: B.
Contained By:	Dissertation Abstracts International75-12B(E).
標題:	Engineering, Chemical. -
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3582667
ISBN:	9781321209914

Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques.
Ebrahimpour, Omid.

Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques. - 203 p.

Source: Dissertation Abstracts International, Volume: 75-12(E), Section: B.

Thesis (Ph.D.)--Ecole Polytechnique, Montreal (Canada), 2014.

This item must not be sold to any third party vendors.

In this work, mullite-bonded porous silicon carbide (SiC) ceramics were prepared via a reaction bonding technique with the assistance of a sol-gel technique or in-situ polymerization as well as a combination of these techniques. In a typical procedure, SiC particles were first coated by alumina using calcined powder and alumina sol via a sol-gel technique followed by drying and passing through a screen. Subsequently, they were coated with the desired amount of polyethylene via an in-situ polymerization technique in a slurry phase reactor using a Ziegler-Natta catalyst. Afterward, the coated powders were dried again and passed through a screen before being pressed into a rectangular mold to make a green body. During the heating process, the polyethylene was burnt out to form pores at a temperature of about 500°C. Increasing the temperature above 800°C led to the partial oxidation of SiC particles to silica. At higher temperatures (above 1400°C) derived silica reacted with alumina to form mullite, which bonds SiC particles together. The porous SiC specimens were characterized with various techniques.

ISBN: 9781321209914Subjects--Topical Terms:

1018531
Engineering, Chemical.

Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques.
LDR:06213nmm a2200361 4500 001 2056195
005 20150505071903.5
008 170521s2014 ||||||||||||||||| ||eng d
020 $a 9781321209914
035 $a (MiAaPQ)AAI3582667
035 $a AAI3582667
040 $a MiAaPQ $c MiAaPQ
100 1 $a Ebrahimpour, Omid. $3 3169939
245 1 0 $a Fabrication of mullite-bonded porous SiC ceramics from multilayer-coated SiC particles through sol-gel and in-situ polymerization techniques.
300 $a 203 p.
500 $a Source: Dissertation Abstracts International, Volume: 75-12(E), Section: B.
500 $a Advisers: Jamal Chaouki; Charles Dubois.
502 $a Thesis (Ph.D.)--Ecole Polytechnique, Montreal (Canada), 2014.
506 $a This item must not be sold to any third party vendors.
506 $a This item must not be added to any third party search indexes.
520 $a In this work, mullite-bonded porous silicon carbide (SiC) ceramics were prepared via a reaction bonding technique with the assistance of a sol-gel technique or in-situ polymerization as well as a combination of these techniques. In a typical procedure, SiC particles were first coated by alumina using calcined powder and alumina sol via a sol-gel technique followed by drying and passing through a screen. Subsequently, they were coated with the desired amount of polyethylene via an in-situ polymerization technique in a slurry phase reactor using a Ziegler-Natta catalyst. Afterward, the coated powders were dried again and passed through a screen before being pressed into a rectangular mold to make a green body. During the heating process, the polyethylene was burnt out to form pores at a temperature of about 500°C. Increasing the temperature above 800°C led to the partial oxidation of SiC particles to silica. At higher temperatures (above 1400°C) derived silica reacted with alumina to form mullite, which bonds SiC particles together. The porous SiC specimens were characterized with various techniques.
520 $a The first part of the project was devoted to investigating the oxidation of SiC particles using a Thermogravimetric analysis (TGA) apparatus. The effects of particle size (micro and nano) and oxidation temperature (910°C--1010°C) as well as the initial mass of SiC particles in TGA on the oxidation behaviour of SiC powders were evaluated. To illustrate the oxidation rate of SiC in the packed bed state, a new kinetic model, which takes into account all of the diffusion steps (bulk, inter and intra particle diffusion) and surface oxidation rate, was proposed. Furthermore, the oxidation of SiC particles was analyzed by the X-ray Diffraction (XRD) technique.
520 $a The effect of different alumina sources (calcined Al2O 3, alumina sol or a combination of the two) on the mechanical, physical, and crystalline structure of mullite-bonded porous SiC ceramics was studied in the second part of the project. Alumina sol was synthesized by the hydrolysis of Aluminum isopropoxide using the Yoldas method. Alumina sol was homogenous and had a needle-like shape with a thickness of 2--3 nm. Crystalline changes during the heating process of alumina sol were studied using XRD. In addition, Fourier transform infrared (FTIR) spectroscopy was performed to identify the functional groups on the alumina sol surface as a function of temperature.
520 $a In the third part of the project, the feasibility of the in-situ polymerization technique was investigated to fabricate porous SiC ceramics. In this part, the mixture of SiC and calcined alumina powders were coated by polyethylene via in-situ polymerizing referred to as the polymerization compounding process in a slurry phase. The polymerization was conducted under very moderate operational conditions using the Ziegler-Natta catalyst system. Differential scanning calorimetry (DSC) and TGA analysis and morphological studies (SEM and TEM) revealed the presence of a high density of polyethylene on the surface of SiC and alumina powders. The amount of polymer was controlled by the polymerization reaction time. Most parts of particles were coated by a thin layer of polyethylene and polymer. The porous SiC ceramics, which were fabricated by these treated particles showed higher mechanical and physical properties compared to the samples made without any treatment. The relative intensity of mullite was higher compared to the samples prepared by the traditional process. The effects of the sintering temperature, forming pressure and polymer content were also studied on the physical and mechanical properties of the final product.
520 $a In the last phase of this research work, the focus of the investigation was to take advantage of both the sol-gel processing and in-situ polymerization method to develop a new process to manufacture mullite-bonded porous SiC ceramic with enhanced mechanical and physical properties. Therefore, first the SiC particles and alumina nano powders were mixed in alumina sol to adjust the alumina weight to 35 wt%. Then, the desired amount of catalyst, which depends on the total surface area of the particles, was grafted onto the surface of the powders under an inert atmosphere. Consequently, the polymerization started from the surface of the substrate. The treated powders were characterized by SEM, XPS and TGA. In addition, the amount of pore-former was determined by TGA analysis. Porous SiC ceramics, which were fabricated by the novel process, consist of mullite, SiC, cristobalite and a small amount of alumina and TiO 2 as a result of reaction of TiCl4 with air. Furthermore, the effect of the sintering temperatures (1500°C, 1550°C and 1600°C) on the crystalline structure of the porous samples was investigated. Furthermore, it was proposed that converting TiCl4 to TiO2 acted as the sintering additive to form mullite at a lower sintering temperature. (Abstract shortened by UMI.).
590 $a School code: 1105.
650 4 $a Engineering, Chemical. $3 1018531
650 4 $a Engineering, Materials Science. $3 1017759
650 4 $a Chemistry, Polymer. $3 1018428
690 $a 0542
690 $a 0794
690 $a 0495
710 2 $a Ecole Polytechnique, Montreal (Canada). $b Genie Chimique. $3 3169940
773 0 $t Dissertation Abstracts International $g 75-12B(E).
790 $a 1105
791 $a Ph.D.
792 $a 2014
793 $a English
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3582667