Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete.

紀錄類型:	書目-電子資源 : Monograph/item
正題名/作者:	Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete./
作者:	Nam, Jingak.
面頁冊數:	125 p.
附註:	Source: Dissertation Abstracts International, Volume: 65-06, Section: B, page: 3095.
Contained By:	Dissertation Abstracts International65-06B.
標題:	Engineering, Materials Science. -
電子資源:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3137076
ISBN:	0496842684

Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete.
Nam, Jingak.

Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete. - 125 p.

Source: Dissertation Abstracts International, Volume: 65-06, Section: B, page: 3095.

Thesis (Ph.D.)--Florida Atlantic University, 2004.

Effects of (1) cement alkalinity (low, normal and high), (2) exposure conditions (RH and temperature), (3) rebar surface condition (as-received versus cleaned) and (4) density and distribution of air voids at the steel-concrete interface on the chloride threshold and time-to-corrosion for reinforcing steel in concrete have been studied. Also, experiments were performed to evaluate effects of RH and temperature on the diffusion of chloride in concrete and develop a method for ex-situ pH measurement of concrete pore water. Once specimens were fabricated and exposed to a corrosive chloride solution, various experimental techniques were employed to determine time-to-corrosion, chloride threshold, diffusion coefficient and void density along the rebar trace as well as pore water pH. Based upon the resultant data, several findings related to the above parameters have been obtained as summarized below.

ISBN: 0496842684Subjects--Topical Terms:

1017759
Engineering, Materials Science.

Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete.
LDR:03403nmm 2200301 4500 001 1849794
005 20051203081252.5
008 130614s2004 eng d
020 $a 0496842684
035 $a (UnM)AAI3137076
035 $a AAI3137076
040 $a UnM $c UnM
100 1 $a Nam, Jingak. $3 1937730
245 1 0 $a Effects of cement alkalinity, exposure conditions and steel-concrete interface on the time-to-corrosion and chloride threshold for reinforcing steel in concrete.
300 $a 125 p.
500 $a Source: Dissertation Abstracts International, Volume: 65-06, Section: B, page: 3095.
500 $a Adviser: William H. Hartt.
502 $a Thesis (Ph.D.)--Florida Atlantic University, 2004.
520 $a Effects of (1) cement alkalinity (low, normal and high), (2) exposure conditions (RH and temperature), (3) rebar surface condition (as-received versus cleaned) and (4) density and distribution of air voids at the steel-concrete interface on the chloride threshold and time-to-corrosion for reinforcing steel in concrete have been studied. Also, experiments were performed to evaluate effects of RH and temperature on the diffusion of chloride in concrete and develop a method for ex-situ pH measurement of concrete pore water. Once specimens were fabricated and exposed to a corrosive chloride solution, various experimental techniques were employed to determine time-to-corrosion, chloride threshold, diffusion coefficient and void density along the rebar trace as well as pore water pH. Based upon the resultant data, several findings related to the above parameters have been obtained as summarized below.
520 $a First, time for the corrosion initiation was longest for G109 concrete specimens with high alkalinity cement (HA). Also, chloride threshold increased with increasing time-to-corrosion and cement alkalinity. Consequently, the HA specimens exhibited the highest chloride threshold compared to low and normal alkalinity ones. Second, high temperature and temperature variations reduced time-to-corrosion of reinforcing steel in concrete since chloride diffusion was accelerated at higher temperature and possibly by temperature variations. The lowest chloride threshold values were found for outdoor exposed specimens suggesting that variation of RH or temperature (or both) facilitated rapid chloride diffusion. Third, an elevated time-to-corrosion and chloride threshold values were found for the wire brushed steel specimens compared to as-received ones. The higher ratio of [OH-]/[Fe n+] on the wire brushed steel surface compared to that of as-received case can be the possible cause because the higher ratio of this parameter enables the formation of a more protective passive film on the rebar. Fourth, voids at the steel-concrete interface facilitated passive film breakdown and onset of localized corrosion. This tendency for corrosion initiation increased in proportion to void size irrespective of specimen type. Also, [Cl -]th decreased with increasing void diameter. In addition, new ex-situ leaching method for determining concrete pore water alkalinity was developed.
590 $a School code: 0119.
650 4 $a Engineering, Materials Science. $3 1017759
650 4 $a Engineering, Marine and Ocean. $3 1019064
650 4 $a Engineering, Civil. $3 783781
690 $a 0794
690 $a 0547
690 $a 0543
710 2 0 $a Florida Atlantic University. $3 1017837
773 0 $t Dissertation Abstracts International $g 65-06B.
790 1 0 $a Hartt, William H., $e advisor
790 $a 0119
791 $a Ph.D.
792 $a 2004
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=3137076